1.96 g/cm³
23 °C
ISO 1183
0.60 %
3 mm
80x80x3mm
Internal Method
0.20 %
3 mm
80x80x3mm
Internal Method
0.020 %
24 hr
23 °C
ISO 62
123
ISO 2039-2
155 MPa
23 °C
ISO 527-2
1.0 %
23 °C
ISO 527-2
20000 MPa
23 °C
ISO 178
245 MPa
23 °C
ISO 178
60.0 MPa
23 °C
JIS K7214
0.30
vs. Metal
70.0 mg
1000 Cycles
ISO 9352
9.0 kJ/m²
23 °C
ISO 179
22 kJ/m²
23 °C
ISO 179
260 °C
1.8 MPa
ISO 75-2/A
1.8E-5 cm/cm/°C
ISO 11359-2
2.7E-5 cm/cm/°C
ISO 11359-2
V-0
0.73 mm
UL 94
1.0e+14 ohms·cm
IEC 60093
22 kV/mm
IEC 60243-1
4.90
60% RH
23 °C
1 MHz
IEC 60250
2.0E-3
60% RH
23 °C
1 MHz
IEC 60250