物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 1.13 g/cm³ | ISO 1183 | |
比重 | 1.13 - | ASTM D792 | |
收缩率 | |||
- | 0.9 % | Internal | 3.18 mm |
吸水率 | 1.6 % | ASTM D570 | 24 hr |
吸水率 | 2.6 % | ASTM D570 | 50% RH |
吸水率 | 9.3 % | ASTM D570 | Saturation |
吸水率 | 1.6 % | ISO 62 | 24 hr |
吸水率 | 2.6 % | ISO 62 | 50% RH |
吸水率 | 9.3 % | ISO 62 | Saturation |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 142 Mpa | ASTM D638 | Conditioned,-40℃ |
屈服(yld) | 25 Mpa | ASTM D638 | Conditioned,121℃ |
屈服(yld) | 48 Mpa | ASTM D638 | Conditioned,23℃ |
屈服(yld) | 30 Mpa | ASTM D638 | Conditioned,80℃ |
屈服(yld) | 137 Mpa | ASTM D638 | Dry,-40℃ |
屈服(yld) | 30 Mpa | ASTM D638 | Dry,121℃ |
屈服(yld) | 90 Mpa | ASTM D638 | Dry,23℃ |
屈服(yld) | 40 Mpa | ASTM D638 | Dry,80℃ |
屈服(yld) | 142 Mpa | ISO 527 | Conditioned,-40℃ |
屈服(yld) | 25 Mpa | ISO 527 | Conditioned,120℃ |
屈服(yld) | 43 Mpa | ISO 527 | Conditioned,23℃ |
屈服(yld) | 30 Mpa | ISO 527 | Conditioned,80℃ |
屈服(yld) | 137 Mpa | ISO 527 | Dry,-40℃ |
屈服(yld) | 30 Mpa | ISO 527 | Dry,120℃ |
屈服(yld) | 25 Mpa | ISO 527 | Dry,150℃ |
屈服(yld) | 88 Mpa | ISO 527 | Dry,23℃ |
屈服(yld) | 40 Mpa | ISO 527 | Dry,80℃ |
断裂(brk) | 80 Mpa | ASTM D638 | Conditioned,-40℃ |
断裂(brk) | 20 Mpa | ASTM D638 | Conditioned,121℃ |
断裂(brk) | 70 Mpa | ASTM D638 | Conditioned,23℃ |
断裂(brk) | 30 Mpa | ASTM D638 | Conditioned,80℃ |
断裂(brk) | 130 Mpa | ASTM D638 | Dry,-40℃ |
断裂(brk) | 25 Mpa | ASTM D638 | Dry,121℃ |
断裂(brk) | 90 Mpa | ASTM D638 | Dry,23℃ |
断裂(brk) | 35 Mpa | ASTM D638 | Dry,80℃ |