1.20 g/cm³
ASTM D792
ISO 1183
1.20 cm³/g
ASTM D792
16 g/10min
250 °C
5 kg
ASTM D1238
ISO 1133
0.80 - 1.0 %
3.2 mm
Internal Method
0.80 - 1.0 %
3.2 mm
Internal Method
79
ISO 868
1980 MPa
5 mm/min
ASTM D638
2010 MPa
50 mm/min
ASTM D638
2070 MPa
ISO 527-2/1
48.0 MPa
50 mm/min
Type I
ASTM D638
45.0 MPa
5 mm/min
Type I
ASTM D638
52.0 MPa
ISO 527-2/50
46.0 MPa
5 mm/min
Type I
ASTM D638
47.0 MPa
50 mm/min
Type I
ASTM D638
50.0 MPa
ISO 527-2/50
4.1 %
5 mm/min
Type I
ASTM D638
4.2 %
50 mm/min
Type I
ASTM D638
4.5 %
ISO 527-2/50
110 %
5 mm/min
Type I
ASTM D638
120 %
50 mm/min
Type I
ASTM D638
120 %
ISO 527-2/50
1900 MPa
1.3 mm/min
50 mm span
ASTM D790